In metallurgy, Stainless steel is defined[1] as a ferrous alloy with a minimum of 10.5% chromium content. Such steels have higher resistance to oxidation (rust) and corrosion in several environments. It was invented in 1912, at the research laboratory of Brown-Firth[?], Sheffield, England by Harry Brearley[?]. He had been investigating ways to reduce corrosion in gun-barrels, when it was noticed that a discarded sample was not rusting.
High oxidation resistance in air at ambient temperature is normally achieved with additions of more than 12%(weight) chromium. The chromium forms a layer of chromium (III) oxide (Cr2O3) when exposed to oxygen. The layer is too thin to be visible, meaning the metal stays shiny. It is, however, impervious to water and air, protecting the metal beneath. Also, when the surface is scratched this layer quickly reforms. When stainless steel parts such as nuts and bolts are forced together, the oxide layer can be scraped off causing the parts to weld together. This effect is known as galling[?].
There are different types of stainless steels: when nickel, for instance is added the austenite structure of iron is stabilized and these steels become non-magnetic. For higher hardness and strength, carbon is added. When subjected to adequate heat treatment these steels[?] are used as razor blades, cutlery, tools etc.
In recent decades, significant quantities of manganese have come to be used in many stainless steel recipes. Manganese imparts similar qualities to the steel as does nickel, but at a lower cost.
Stainless steels are also classified by their crystalline structure:
- Austenitic stainless steels comprise over 70% of total stainless steel production. They contain a maximum of 0.15% carbon, a minimum of 16% chromium and sufficient nickel and/or manganese to retain an austenitic structure at all temperatures from the cryogenic region to the melting point of the alloy. A typical composition is 18% chromium and 8% nickel, commonly known as 18/8 stainless.
- Ferritic stainless steels are highly corrosion resistant, but far less durable than austenitic grades and cannot be hardened by heat treatment. They contain between 10.5% and 27% chromium and very little nickel, if any. Most recipes include Molybdenum; some, aluminum or titanium. Common ferritic grades include 18Cr-2Mo, 26Cr-1Mo, 29Cr-4Mo, and 29Cr-4Mo-2Ni.
- Martensitic stainless steels are not as corrosion resistant as the other two classes, but are extremely strong and tough as well as highly machineable, and can be hardened by heat treatment. They contain 11.5 to 18% chromium and significant amounts of carbon. Some grades include additional alloying elements in small quantities.
The AISI defines the following grades:
- 200 Series - austeniitic iron-chromium-nickel-manganese alloys
- 300 Series - austeniitic iron-chromium-nickel alloys
- Type 301 - highly ductile, for formed products
- Type 303 - equivalent to ISO [2] A1.
- Type 304 - the most common; austenitic (contains nickel); equivalent to ISO A2.
- Type 316 - for food and medical uses; contains nickel and molybdenum; also called 18-8; equivalent to ISO A4.
- 400 Series - ferritic and martensitic alloys
- Type 408 - heat-resistant; poor corrosion resistance; 11% chromium, 8% nickel.
- Type 409 - cheapest type; used for automobile exhausts; ferritic (iron/chromium only).
- Type 410 - martensitic (high-strength iron/chromium); equivalent to ISO C1.
- Type 420 - "Cutlery[?] Grade" martensitic; similar to the Brearley's original "rustless steel".
- Type 430 - decorative, e.g. for automotive trim; ferritic.
References
Common misspelling and questions (FAQ)
tainless-steel sainless-steel stinless-steel stanless-steel stailess-steel stainess-steel stainlss-steel stainles-steel stainles-steel stainlesssteel stainless-teel stainless-seel stainless-stel stainless-stel stainless-stee tsainless-steel satinless-steel stianless-steel staniless-steel stailness-steel stainelss-steel stainlses-steel stainless-steel stainles-ssteel stainlesss-teel stainless-tseel stainless-setel stainless-steel stainless-stele stainless-stee sstainless-steel sttainless-steel staainless-steel staiinless-steel stainnless-steel stainlless-steel stainleess-steel stainlesss-steel stainlesss-steel stainless--steel stainless-ssteel stainless-stteel stainless-steeel stainless-steeel stainless-steell wtainless-steel atainless-steel ztainless-steel etainless-steel xtainless-steel etainless-steel dtainless-steel xtainless-steel s5ainless-steel srainless-steel sfainless-steel s6ainless-steel sgainless-steel s6ainless-steel syainless-steel sgainless-steel stqinless-steel stwinless-steel stzinless-steel stwinless-steel stsinless-steel stzinless-steel sta8nless-steel staunless-steel stajnless-steel sta9nless-steel staknless-steel sta9nless-steel staonless-steel staknless-steel staihless-steel staibless-steel staijless-steel staijless-steel staimless-steel stainoess-steel stainkess-steel stain,ess-steel stainpess-steel stain.ess-steel stainpess-steel stain;ess-steel stain.ess-steel stainl3ss-steel stainlwss-steel stainlsss-steel stainl4ss-steel stainldss-steel stainl4ss-steel stainlrss-steel stainldss-steel stainlews-steel stainleas-steel stainlezs-steel stainlees-steel stainlexs-steel stainlees-steel stainleds-steel stainlexs-steel stainlesw-steel stainlesa-steel stainlesz-steel stainlese-steel stainlesx-steel stainlese-steel stainlesd-steel stainlesx-steel stainless0steel stainlesspsteel stainless[steel stainless-wteel stainless-ateel stainless-zteel stainless-eteel stainless-xteel stainless-eteel stainless-dteel stainless-xteel stainless-s5eel stainless-sreel stainless-sfeel stainless-s6eel stainless-sgeel stainless-s6eel stainless-syeel stainless-sgeel stainless-st3el stainless-stwel stainless-stsel stainless-st4el stainless-stdel stainless-st4el stainless-strel stainless-stdel stainless-ste3l stainless-stewl stainless-stesl stainless-ste4l stainless-stedl stainless-ste4l stainless-sterl stainless-stedl stainless-steeo stainless-steek stainless-stee, stainless-steep stainless-stee. stainless-steep stainless-stee; stainless-stee. staynless-steel stainles-steel syainless-steel styainless-steel stainless-steelsWhich we do follow, fierce, yet laughing, And at the last shall we bring thee up Of lily folden, Swift thy starr'd feet as wing of swallow, And at the last shall we draw near, Woven of roses, of stars, of songs? Of rare gems olden!" They hung the slaughter'd fish like swords Bright, and ruddied from new-dead wars, Of cedar-web and green fir tassel; The camp fire blush'd to the tender breeze. The hounds laid dew-laps on the ground, Dream'd of the dead stag stout and lusty; Close round the camp, and at its curtain As white locks of tall waterfalls. Ae blink o' the bonnie new mune, Wad licht me to Meg frae the toun, Ae fuff o' the saftest o' win's, Wad blaw me o'er knaggies an' linns-- My mither had kin at the court; Or any sic frolicsome sport. Wi' bodies an' gear i' her loof-- Hell glunsh at himsel' for a coof! My daddie's na doylt, tho' he's auld, When the lammies are pit i' the fauld, My mither sits spinnin'--ae blink She's minded o' mony a link Tentie jinkin' by lea an' by shaw; So I may steal cannie awa'. An' the blink o' the bonnie new mune! That trots like a burnie in June! My Meg she is waitin' abeigh-- Wad jealously lead me astray .